External Wall Insulation Stone Wool Insulation Board / Panel / Slab / Sheet Eco-Friendly WD-DI03 manufacturer from China Shanghai Weidi Industrial Company

External Wall Insulation Stone Wool Insulation Board / Panel / Slab / Sheet Eco-Friendly

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: WD-DI03

New types decorative plates used for external wall insulation and decoration with good weather ability and Anti pollution

Specifications:

Product			Performance
Metal Fluorocarbon Painting Decorative Insulation Board	Decoration Layer	Rock slice real mineral paint decorative board	Superior adhesion, water resistance, stain resistance, weather resistance, colorful	Real mineral paint mainly composed of polymers, natural stones& sand and related auxiliaries, hard as stone after dry , looks like natural stone
	Insulation Layer	EPS insulation layer (Grade B1)	Heat conductivity ≤0.041. volume-weight :18kg / m³ with the tensile strength:110--120kpa; volume-weight 20kg / m³ with the tensile strength :140kpa.
		XPS insulation Layer (Grade B1)	Heat conductivity ≤0.030. Volume-weight 25--45kg / m³ & tensile ≥150kpa. Strong compressive resistance. 30-40 years average using life. Excenllent structure load-bearing performance .
		Polyurethane insulation board (Grade B1)	Hard polyurethane with low thermal conductivity, good thermal performance. When the hard polyurethane with the density of 35 ~ 40kg / m3, thermal conductivity is only 0.018 ~ 0.024w / (m.k), equivalent to half of the EPS, is the lowest heat conductivity of all the insulation materials .
		TPS insulation board (Grade B1)	Heat insulation thermal conductivity is 0.060W / (m · k) ,it has good tensile compressive strength , impact resistance and stability ; its compressive strength reaches 150-500KPa
		Rock wool (Grade A)	Appearance quality: smooth surface, without prejudice practical scars, stains damaged. Combustion performance: non-combustible. Thermal load contraction temperature: 643 degrees. Moisture absorption: 3.9%. Organic content: 2.9%. Rockwool board basic parameters: Material: rockwool Apparent density: Rockwool 120 (kg / m3) Heat conductivity: 0.04 (W / (m.K)) Max operating temperature: 80 () Specifications: 950,1150 (mm ) Operation standard: GB Operating temperature: 80 ()
		Phenolic Foam Board(Grade B Grade A)	Not be melt at high temperatures ,not be softened, with low smoke, non-proliferation flame resistance, flame penetration, There is no distortion, no burning ,no fire, being placed 10 minutes at 1400 , can effectively prevent the flames and smoke spread

Weidi Decorative Insulation Board final product facing layer performance

(varieties: solid color/metal/stone/wood grain/special effects, etc.)

Test Item	Detection standard and requirements		The third party test results
Coating thickness(μm)	GB/T13452.2- 2008-10	≥30	199
Coating adhesion(MPa)	GB/T5210-2006	≥0.3	1.7(0.8-2.7),100%A
Hardness(Pencil)	GB/T6739-2006	≥4H	6H No scraping damage
Abrasive resistance(750g/500r) ,Suitable grinding wheel type:CS-10	GB/T1768-2006		0.003
Solvent resistance wiping(Butanone, 100times)	HC/T-3792-2005 Appendix	No undercasing	Meet the requirement
Acid-resistance(5%HC1 liquor,24H)	GB/T9274-1998	No blistering,No Falling off,non-discolouring	No Change
Alkali resistance	GB/T9274-1998	No blistering,No Falling off,non-discolouring	No Change
Abrasion performance	HC/T3793-2005- 4.1/4.3	≥5	12
Stain resistance	GB/T9757-2001 Appendix A	≤5	5
Scrub resistance	GB/T9266-2009	≥10000	>10000
Oil resistant(Immerse in engine oil SE15W-40 24H)	GB/T9274-198888	No blistering,No Falling off,non-discolouring	No Change
Alkali burnout resistance(72H)	JG/T210-2007		No abnormalities
Salting-out resistance(144H)	JG/T210-2007		No abnormalities
Weather resistance	GB/T1865-2009,GB/T1766-2008	Artificial climate ageing and radiation exposure	4000Hrs after testing,Dulling≤3Grade, Discoloration≤2Grade