Metal Fluorocarbon External Wall Decorative Insulation Board Soundproof And Waterproof WD-DI01 manufacturer from China Shanghai Weidi Industrial Company

Metal Fluorocarbon External Wall Decorative Insulation Board Soundproof And Waterproof

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: WD-DI01

Metal fluorocarbon wall Insulation board used for external wall decoration

Weidi Decorative Insul

Metal fluorocarbon wall Insulation board used for external wall decoration

Weidi Decorative Insulation Board system performance index

Item	Detection standard and requirements			The third party test results
Weather resistance	JF149-2003, JGG144-2004		After weather resistance test, No damage such as facing layer blistering or falling off,Protective layer hollowing or falling off; No seepage crack appear.	No damage such as facing layer blistering or falling off,Protective layer hollowing or falling off; No seepage crack
Weather resistance	JG149-2003, JGJ144-2004			Impact-resistance strength grade:10
Water absorption g/,Immersed 24H	JG149-2003, JGJ144-2004		≤500	21
Wind pressure resistance value KPa	JG149-2003, JGJ144-2004		Not less than the wind load design value of the project	After 15 kpa level wind load esistance test,,no water seepage
Freezing and thawing resistance	JG149-2003, JGJ144-2004		No surface cracking,hollowing, blistering,exfoliation	No surface cracking, hollowing,blistering, exfoliation
Steam flow density g/(·H)	JG149-2003, JGJ144-2004		≥0.85	2.36
Watertightness	JG149-2003, JGJ144-2004		Sample protective layer inside without water infiltration	Sample protective layer insidewithout water infiltration
Thermal conductivity W/(m·k)	GB/T10801.1-2002, JG149-2003		≤0.041	0.033
Apparent density kg/m³	GB/T10801.1-2002, JG149-2003		18.0-22.0	19
The compressive strength perpendicular to the panel MPa	GB/T10801.1-2002, JG149-2003		≥0.10	0.10
Dimensional stability %	GB/T10801.1-2002, JG149-2003		≤0.30	Length Change 0.13
				Width Change 0.15
				Thickness Change 0.24
Compression strength KPa	GB/T10801.1-2002, JG149-2003		≥60	99
Water vapor permeability ng/(Pa··s)	GB/T10801.1-2002, JG149-2003		≤60	4
Water absorption (Volume fraction)%	GB/T10801.1-2002, JG149-2003		≤6	2
Tensile bond strength MPa (Connected with cement mortar)	Original intensity	JG149-2003	≥0.60	0.94
Tensile bond strength MPa (Connected with cement mortar)	Water resistant	JG149-2003	≥0.40	0.54
Tensile bond strength MPa (Connected with Expanded polyphenyl board)	Original intensity	JG149-2003	≥0.10,Destroy interface on EPS Board	≥0.10,Destroy interface on EPS Board
	Water resistant	JG149-2003	≥0.10,Destroy interface on EPS Board	≥0.10,Destroy interface on EPS Board
Operational time H	JG149-2003		1.5-4.0	4.0
Single anchor bolt tensile standard capacity KN	JG149-2003		≥0.30	0.83